Strenx performance steel

Strenx® 100

Download data sheet

General Product Description

Strenx® 100 is a structural steel with a minimum yield strength of 690 Mpa. Strenx® 100 meets the requirements of ASTM A514, Grade S,

for thicknesses up to 63.50 mm.

Dimension Range

Strenx® 100 is supplied in plate thicknesses of 4.762 - 127.0 mm. More detailed information on dimensions is provided in the dimension program at www.ssab.com.

Mechanical Properties

Thickness
(mmin)
Thickness
(mmin)
4.76 - 19.050.1875 - 0.7500
Yield strength Rp0.2
(min MPaksi)
690100
Tensile strength Rm
(MPaksi)
760 - 890110 - 130
Elongation A50 1)
(min %)
16
Reduction of area
(min %)
35
Thickness
(mmin)
Thickness
(mmin)
19.06 - 63.500.7500 - 2.500
Yield strength Rp0.2
(min MPaksi)
690100
Tensile strength Rm
(MPaksi)
760 - 890110 - 130
Elongation A50 1)
(min %)
16
Reduction of area
(min %)
35 2)
Thickness
(mmin)
Thickness
(mmin)
63.51 - 101.602.500 - 4
Yield strength Rp0.2
(min MPaksi)
65094
Tensile strength Rm
(MPaksi)
700 - 890110 - 130
Elongation A50 1)
(min %)
14
Reduction of area
(min %)
35 2)
Thickness
(mmin)
Thickness
(mmin)
101.61 - 127.004 - 5
Yield strength Rp0.2
(min MPaksi)
65094
Tensile strength Rm
(MPaksi)
700 - 890102 - 130
Elongation A50 1)
(min %)
14
Reduction of area
(min %)
35 2)

1) For transverse test pieces according to ASTM A6 and A370.

2) For 1-1/2” wide tension test samples. If 1/2” round samples are used, the minimum RA is 45%.

Impact Properties

Product
Product
Strenx® 100
Min impact energy for transversal testing,
Charpy V 0.393x0.393" test specimen 1)
67 J / -40 °C50 ft-lbs / -40 °F

1) Average of three tests. Single value min 2/3 of specified average.

For thicknesses between 6 - 11.9 mm, sub-size Charpy V-specimens are used. The specified minimum value is then proportrional to the cross-sectional area of the specimen compared to a full-size specimen (10x10 mm).

Chemical Composition (ladle analysis)

C *)
(max %)
C *)
(max %)
0.20
Si *)
(max %)
0.60
Mn*)
(max %)
1.60
P
(max %)
0.020
S
(max %)
0.010
Cr*)
(max %)
0.80
Ni*)
(max %)
2.0
Mo*)
(max %)
0.70
B*)
(max %)
0.005

The steel is grain refined. *) Intentional alloying elements.

Carbon Equivalent CET(CEV)

Thickness (mmin)
Thickness (mmin)
Max CET(CEV)
4.762 - 31.7500.1875 - 1.250
0.32 (0.46)
31.751 - 50.8001.250 - 2
0.36 (0.52)
50.801 - 101.6002 - 4
0.39 (0.58)
101.601 - 127.004 - 5
0.41 (0.67)

Tolerances

More details are given in SSAB’s brochure Strenx® Guarantees.

Thickness

Tolerances according to Strenx® Thickness Guarantees.
Strenx® Guarantees meets the requirements of EN 10029 Class A, but offers narrower tolerances.
EN 10029 meets and exceeds the requirements for ASTM A6.

Length and Width

Tolerances on length and width according to ASTM A6.

Shape

Flatness

Tolerances on flatness according to Strenx® Flatness guarantee Class C, which are twice as good as the ASTM A6 flatness requirements. 

Surface Properties

According to ASTM A6.

Delivery Conditions

The delivery condition is Quenched and Tempered. The plates are delivered with sheared or thermally cut edges. Untrimmed edges after agreement.

Delivery requirements can be found in SSAB’s brochure Strenx® Guarantees.

Fabrication and Other Recommendations

Welding, bending and machining

Recommendations are found in SSAB’s brochures at www.ssab.com or consult Tech Support.

Workshop guidelines for Strenx® 100 refer to the same recommendations as for Strenx® 700. Bending guarantees according to Strenx® bending guarante class A.

Strenx® 100 has obtained its mechanical properties by quenching and subsequent tempering. The properties of the delivery condition cannot be retained after exposure to temperatures in excess of 580ºC.