Docol® 700LA high strength low alloy

More about high strength low alloy steel

Download data sheet

Select Language

General Product Description

The Docol 700LA steels are high-strength low-alloy steels that offer consistent properties for modern, rapid production methods. The Docol 700LA steels are made for cold forming of stronger and lighter structures. Typical applications include components and parts in demanding load-bearing structures such as chassis. Docol HR700LA-UC can after agreement be adapted and delivered as dual certified with S700MC according to EN 10149-2.

Dimension Range

Hot rolled / UC: thickness 2.00-6.00 mm, width up to 1600 mm.

Hot rolled / EG: thickness 2.00-3.00 mm, width up to 1360 mm.

Hot rolled / GI: thickness 2.00-4.00 mm, width up to 1400 mm.

Slit strip and cut to length sheets are available upon request.

Grade and coating specific restrictions on available dimensions may occur.

Mechanical Properties

	Standard	Coating	Test direction	Yield strength R_p0.2 (MPa)	Tensile strength R_m (MPa)	Elongation A₈₀¹⁾ (min %)	Elongation A₅³⁾ (min %)	Min. inner bending radius for a 90° bend⁴⁾
Docol HR700LA	VDA 239-100	UC, EG	L	700 - 850	750 - 950	10	13	1.2 x t
Docol HR700LA	VDA 239-100	GI*	L	700 - 850	750 - 950	10 ²⁾	—	1.2 x t

Docol HR700LA

Standard

VDA 239-100

Coating

UC, EG

Test direction

Yield strength R_p0.2
(MPa)

700 - 850

Tensile strength R_m
(MPa)

750 - 950

Elongation A₈₀¹⁾
(min %)

Elongation A₅³⁾
(min %)

Min. inner bending radius for a 90° bend⁴⁾

1.2 x t

The testing of mechanical properties of electro galvanized products is conducted without coating.

* Available upon request.

¹⁾ A₈₀ value applies for thicknesses < 3.00 mm.

²⁾ For GI coatings the minimum elongation value is reduced by 1 unit.

³⁾ A₅ value applies for thicknesses ≥ 3.00 mm.

⁴⁾ In some cases tight bending radius may cause micro-cracking of the coating in the bend area. Where design permits, users are encouraged to employ larger radius.

Chemical Composition (ladle analysis)

	Coating	C (max %)	Si (max %)	Mn (max %)	P (max %)	S (max %)	Al (%)	Ti (max %)	Nb (max %)	Cu (max %)
Docol HR700LA	UC, EG, GI*	0.12	0.60	2.10	0.030	0.025	From 0.015	0.20	0.10	0.20

Docol HR700LA

Coating

UC, EG, GI*

C
(max %)

0.12

Si
(max %)

0.60

Mn
(max %)

2.10

P
(max %)

0.030

S
(max %)

0.025

Al
(%)

From 0.015

Ti
(max %)

0.20

Nb
(max %)

0.10

Cu
(max %)

0.20

* Available upon request.

Tolerances

Hot rolled (UC, EG): Tolerances in accordance to EN 10051.

Hot-dip galvanized (GI): Tolerances in accordance to EN 10143.

Customized dimensional and shape tolerances are available upon request.

Coatings

The metal coating options for Docol products include:

Hot-dip zinc coating (GI) consists almost entirely of zinc (>99%). It is lead free, resulting in a small zinc spangle size. The coating provides good corrosion protection.

Electrogalvanized coating (EG) is applied continuously by electro deposition. The coating consists of zinc (>99%). Electrogalvanized steel is characterized by its excellent surface quality and uniform coating thickness.

Grade specific availability of metal coatings for Docol products is given in the Mechanical properties table (Coating).

Coating type	Coating class	Standard	Closest in EN standard, informative ¹⁾	Coating mass per side, single spot test (g/m²)	Thickness per side informative (µm)
GI	40/40	VDA 239-100	Z100	40 - 60 ²⁾	5.6 - 8.5
GI	50/50	VDA 239-100	—	50 - 70 ²⁾	7.0 - 9.9
GI	60/60	VDA 239-100	Z140	60 - 90	8.5 - 12.7
GI	70/70	VDA 239-100	—	70 - 100	9.9 - 14.1
GI	85/85	VDA 239-100	—	85 - 115	12.0 - 16.2
GI	115/115	VDA 239-100	Z275	115 - 155	16.2 - 21.8
EG	12/12	VDA 239-100	ZE25/25	12 - 32	1.7 - 4.5
EG	18/18	VDA 239-100	—	18 - 38	2.5 - 5.4
EG	29/29	VDA 239-100	ZE50/50	29 - 49	4.1 - 6.9
EG	47/47	VDA 239-100	ZE75/75	47 - 61	6.6 - 8.6
EG	50/50	VDA 239-100	—	50 - 70	7.0 - 9.9
EG	53/53	VDA 239-100	—	53 - 73	7.5 - 10.3
EG	60/60	VDA 239-100	—	60 - 80	8.5 - 11.3
EG	65/65	VDA 239-100	ZE100/100	65 - 85	9.2 - 12.0
EG	70/70	VDA 239-100	—	70 - 90	9.9 - 12.7

Coating type

Coating class

40/40

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

Z100

Coating mass per side, single spot test (g/m²)

40 - 60 ²⁾

Thickness per side informative (µm)

5.6 - 8.5

Coating type

Coating class

50/50

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

50 - 70 ²⁾

Thickness per side informative (µm)

7.0 - 9.9

Coating type

Coating class

60/60

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

Z140

Coating mass per side, single spot test (g/m²)

60 - 90

Thickness per side informative (µm)

8.5 - 12.7

Coating type

Coating class

70/70

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

70 - 100

Thickness per side informative (µm)

9.9 - 14.1

Coating type

Coating class

85/85

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

85 - 115

Thickness per side informative (µm)

12.0 - 16.2

Coating type

Coating class

115/115

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

Z275

Coating mass per side, single spot test (g/m²)

115 - 155

Thickness per side informative (µm)

16.2 - 21.8

Coating type

Coating class

12/12

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

ZE25/25

Coating mass per side, single spot test (g/m²)

12 - 32

Thickness per side informative (µm)

1.7 - 4.5

Coating type

Coating class

18/18

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

18 - 38

Thickness per side informative (µm)

2.5 - 5.4

Coating type

Coating class

29/29

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

ZE50/50

Coating mass per side, single spot test (g/m²)

29 - 49

Thickness per side informative (µm)

4.1 - 6.9

Coating type

Coating class

47/47

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

ZE75/75

Coating mass per side, single spot test (g/m²)

47 - 61

Thickness per side informative (µm)

6.6 - 8.6

Coating type

Coating class

50/50

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

50 - 70

Thickness per side informative (µm)

7.0 - 9.9

Coating type

Coating class

53/53

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

53 - 73

Thickness per side informative (µm)

7.5 - 10.3

Coating type

Coating class

60/60

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

60 - 80

Thickness per side informative (µm)

8.5 - 11.3

Coating type

Coating class

65/65

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

ZE100/100

Coating mass per side, single spot test (g/m²)

65 - 85

Thickness per side informative (µm)

9.2 - 12.0

Coating type

Coating class

70/70

Standard

VDA 239-100

Closest in EN standard, informative ¹⁾

—

Coating mass per side, single spot test (g/m²)

70 - 90

Thickness per side informative (µm)

9.9 - 12.7

Docol metal coated products are available with surface quality for unexposed applications.

In addition to these coating masses, OEM specific coatings are available upon request.

¹⁾ For GI and GA the closest informative value refers to EN 10346. For EG to EN 10152.

²⁾ For hot-dipped (GI, ZA, GA) hot rolled (HR) grades, the coating mass tolerance is increased to 30 g/m² by increasing the upper limit.

Surface Treatments

Uncoated (UC): available as oiled.

Hot-dip galvanized (GI): available as oiled and/or chemically passivated.

Electrogalvanized (EG): available as oiled and/or chemically passivated or phosphated.

All surface treatments are in accordance with RoHS directive (2011/65/EU) and do not contain Chromium VI (Cr⁶⁺). Surface treatments provide only temporary surface protection during transportation and storage. In order to avoid corrosion damages, care must be taken to keep the products dry during transportation and storage. If they become wet, they must be separated and situated so that they are dried quickly.

Fabrication and Other Recommendations

For information concerning fabrication, see SSAB´s brochures on www.ssab.com or consult Tech Support.

Appropriate health and safety precautions must be taken when bending, welding, cutting, grinding or otherwise working on the products.

Docol® High Strength Low Alloy steel product offer

Docol® 700LA high strength low alloy

General Product Description

Dimension Range

Mechanical Properties

Chemical Composition (ladle analysis)

Tolerances

Coatings

Surface Treatments

Fabrication and Other Recommendations

Docol® High Strength Low Alloy steel product offer

Docol® 420LA high strength low alloy

Docol HR100XF

Docol HR110XF

Docol® S600MC high strength low alloy

Docol® S650MC high strength low alloy

Docol® S700MC high strength low alloy

Docol® S900MC high strength low alloy

Docol S960MC

Docol® 460LA high strength low alloy

Docol® 500LA high strength low alloy

Docol® 550LA high strength low alloy

Docol® 600LA high strength low alloy

Docol® 650LA high strength low alloy

Docol® 700LA high strength low alloy

Related content

AHSS trial material stock

Automotive steel applications

Forming data for Docol® AHSS steels